Bitumen Datasheet
Bitumen 60 70
| test results | |||||||||
| Ambient condition | Temprature (C°) | Pressure (mm Hg) | humidity | ||||||
| 25 | 760 | ||||||||
| NO. | test | time | result | Standard Range | test method | ||||
| min | max | INSO | ASTM | ||||||
| 1 | Specific Gravity 25°C/25°C | 1.01 | 1.06 | 3872 | D70 | ||||
| 2 | Penetration 25°C-100gr-5s,0.1mm | 60 | 70 | 2950 | D5 | ||||
| 3 | Softening Point°C (R&B) | 46 | . | 3868 | D36 | ||||
| 4 | Flash Point°( Cleveland Open Cup) | 230 | . | 198 | D92 | ||||
| 5 | Ductility 25 °5cm/min,cm | 100 | . | 3866 | D113 | ||||
| 6 | Solubility in Trichloroethylene (wt)% | 99 | . | 2953 | D2042 | ||||
| 7 | Spot Test | Ngative | 2949 | AASHTO T102 | |||||
| 8 | Kinemetic viscosity 135°C,mm²/s | . | . | 12855 | D2170 | ||||
| 9 | Dinamic Viscosity 60°C,Pa.s | . | . | 12851 | D2171 | ||||
| 10 | Penetration Index | -1.5 | 0.7 | . | EN12607-1 | ||||
| Thin Film Oven Test , 163° C,3.2 mm , for 5 hours (TFOT) (ASTM D1754) | |||||||||
| 11 | change in mass (wt%) | . | 0.8 | 2957 | D1754 | ||||
| 12 | Penetration after heating 25°-100gr-5s,0.1mm | . | . | 2950 | D5 | ||||
| 13 | Rateiend Penetration % | 52 | . | 2950 | D5 | ||||
| 14 | Ductility After Heating 25°,5cm/min,cm | 50 | . | 3866 | D113 | ||||
| 15 | Dinamic Viscosity 60°C,Pa.s | . | . | 12851 | D2171 | ||||
| Loss On Heating (ASTM D6) | |||||||||
| 16 | Loss On Heating (wt%) | . | 0.2 | . | D6 | ||||
| 17 | Penetration after heating 25°-100gr-5s,0.1mm | . | . | . | D5 | ||||
| 18 | drop in penetration | . | 20 | . | D6 | ||||
Bitumen 85 100
| test results | |||||||||
| Ambient condition | Temprature (C°) | Pressure (mm Hg) | humidity | ||||||
| 25 | 760 | ||||||||
| NO. | test | time | result | Standard Range | test method | ||||
| min | max | INSO | ASTM | ||||||
| 1 | Specific Gravity 25°C/25°C | 1.01 | 1.05 | 3872 | D70 | ||||
| 2 | Penetration 25°C-100gr-5s,0.1mm | 85 | 100 | 2950 | D5 | ||||
| 3 | Softening Point°C (R&B) | 42 | . | 3868 | D36 | ||||
| 4 | Flash Point°( Cleveland Open Cup) | 230 | . | 198 | D92 | ||||
| 5 | Ductility 25 °5cm/min,cm | 100 | . | 3866 | D113 | ||||
| 6 | Solubility in Trichloroethylene (wt)% | 99 | . | 2953 | D2042 | ||||
| 7 | Spot Test | Ngative | 2949 | AASHTO T102 | |||||
| 8 | Kinemetic viscosity 135°C,mm²/s | . | . | 12855 | D2170 | ||||
| 9 | Dinamic Viscosity 60°C,Pa.s | . | . | 12851 | D2171 | ||||
| 10 | Penetration Index | -1.5 | 0.7 | . | EN12607-1 | ||||
| Thin Film Oven Test , 163° C,3.2 mm , for 5 hours (TFOT) (ASTM D1754) | |||||||||
| 11 | change in mass (wt%) | . | 1 | 2957 | D1754 | ||||
| 12 | Penetration after heating 25°-100gr-5s,0.1mm | . | . | 2950 | D5 | ||||
| 13 | Rateiend Penetration % | 47 | . | 2950 | D5 | ||||
| 14 | Ductility After Heating 25°,5cm/min,cm | 75 | . | 3866 | D113 | ||||
| 15 | Dinamic Viscosity 60°C,Pa.s | . | . | 12851 | D2171 | ||||
| Loss On Heating (ASTM D6) | |||||||||
| 16 | Loss On Heating (wt%) | . | 0.5 | . | D6 | ||||
| 17 | Penetration after heating 25°-100gr-5s,0.1mm | . | . | . | D5 | ||||
| 18 | drop in penetration | . | 20 | . | D6 | ||||